Cold galvanizing, also called electric galvanizing, is the use of electrolytic equipment to remove oil, pickling, after the pipe fitting into the composition of zinc salt solution, and connected to the negative electrode of the electrolytic equipment. Wire factory on the opposite side of the pipe fittings placed zinc plate, connected to the positive electrode of the electrolytic equipment is connected to the power supply, the use of current from the positive electrode to the negative electrode will deposit a layer of zinc on the pipe fittings, cold plating pipe fittings is first processed after galvanized.

(2) Packing and binding galvanized shaft wire order notes: ① the galvanized iron wire shall not be damaged when the tightening. (2) Stop the use of more than two strands of galvanized iron wire around the operation method. ③ The diameter of galvanized wire for pulling should not be less than 4mm, and the diameter of galvanized wire for binding should not be less than 2.6mm. (4) Galvanized iron wire shall not be used as waist hoop down reinforcement, usually not used as a whole binding. Warehouse galvanized wire is mainly used to block and distinguish the function of the area, warehouse galvanized wire is one of the primary use of galvanized wire, warehouse galvanized wire primary layout features are as follows: layout: Column mesh frame, column to choose square steel pipe, galvanized wire frame is also a small square pipe as the data, column and mesh frame corresponding direction are welded connecting ear piece (flat iron), column and mesh frame through the connection of the ear piece bolt fixed, column bottom welding plate, column bottom plate through expansion bolts and fixed on the ground.

The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.

In order to pack and bundle galvanized wire on the surface of the deposit layer to remove the surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is caused by soaps and saponable fatty surfactants being brought into the tank. Moderate foam formation rates may be harmless. Small homogeneous particles of large denier present in the tank can stabilize the foam layer. To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the intake of surfactant. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.

Strictly control the pH value of large roll galvanized wire bath, research shows that the size of the bath pH value directly affects the quality of steel wire coating, improper control of pH value will cause loose coating. When the pH value is greater than 3, the steel wire coating has burr caused by fine dendrites, and the surface is not smooth. The current density is strictly controlled. From the microscopic morphology, the higher the current density, the larger the zinc layer grain deposition, the less dense the corresponding zinc layer.

In the calculation process of 12*14 specifications of barbed rope, it can not be calculated according to the above calculation formula, because first of all, two specifications of raw materials are used, the thinner the wire diameter, the higher the processing cost. Generally speaking, a kilogram of 12*14 barbed rope can reach about 7.5 meters, and the ratio of warp wire to barbed rope cannot be calculated according to the traditional ratio of 7 to 3. The specific use of how much wire and silk need to go through a series of professional measurement but also increase the loss of raw materials and other factors to calculate. Thorn rope factory will also according to customer needs to calculate the reasonable amount of customer use.

Common galvanized iron wire equipment is usually used in barbecue net, barbecue net generally requires to have a long service life, with galvanized iron wire equipment to wire a layer of zinc, barbecue net is not easy to be corroded.

The production of large rolls of galvanized wire iron can be divided into two categories, is directly from the iron ore after iron stroke exercise out of the metal, the composition of the ore is iron oxide, silica and other miscellaneous stone.

Large roll galvanized wire is the use of low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes, in the use of is more widely. The temperature of large roll galvanized wire for electroplating should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.