The formation process of hot dip galvanized layer is between the iron matrix and the outside of the pure zinc layer, the formation of iron-zinc alloy process, the workpiece surface in hot dip plating when the formation of iron-zinc alloy layer, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc liquid, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the attraction between the atoms is relatively small.

Its wire diameter specifications include: 8#-24#, with thick coating, corrosion resistance, strong coating and so on. And according to the special needs of users, according to industry standards to provide various specifications of galvanized wire. Low carbon steel wire is called galvanized iron wire after drawing and galvanized, so galvanized wire products have certain characteristics. In order to better let galvanized wire play an effect, in the process of galvanized wire, generally according to customer needs to control the thickness of galvanized wire zinc layer, so that galvanized wire can meet the needs of customers.

Hot drawing is the heating before the wire enters the die hole, mainly used for high melting point wire drawing; The temperature drawing is carried out by heating the heater to the range of temperature, mainly used for galvanized steel wire, difficult to deform drawing.

Different supports are used for different installation environments. In the past, the blade barbed wire was not easy to fix, and the installation environment was often steep. Therefore, special tools must be used to fix the blade barbed wire to prevent it from being improperly installed.

Some customers are more concerned about the quality of the problem, so for the service life is more important, thorn rope factory will generally recommend the use of high zinc thorn rope or stainless steel thorn rope.

In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.