Generally, due to wet weather and more precipitation, oxidation and rust of binding iron wire NetEase occurs, so we should better store and use galvanized iron wire to avoid rust as far as possible. About the barbed wire, the surface of the barbed wire attached a layer of galvanized layer, the galvanized layer if too thick will not meet the SGS environmental standards. But if it is too thin, it is easy to oxidize with water molecules and rust.

The use of electric welding mesh is very wide, can be used in many places. In the field of construction, especially the wall crack, has played a very important role, the traditional construction, is to put on mortar directly onto the wall, after such a long time, will appear fall off and fracture phenomenon, in order to prevent the occurrence of this phenomenon, must use welded wire mesh before rendering, welded wire mesh is fixed to the wall, above the plastering construction, Can ensure that the wall level for a long time, not easy to crack phenomenon.

It is best to use special columns to fix the barbed rope installation, because the standard column is not only beautiful shape and better protection effect.

Specific requirements for the safety of galvanized wire production: clean up all tools and other objects that hinder production in the galvanized wire production environment. Operators in the pickling process, pay attention to the action should be careful, not careless, into the pickling tank must be handled lightly, to prevent splashing on the body. When adding acid, the acid must be slowly poured into the water. It is forbidden to pour the water into the acid, so as to prevent the acid from splashing out and hurting people. Do not hurt yourself or others.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

According to the galvanized iron wire manufacturer, galvanized iron wire is the selection of excellent low carbon steel, through drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized, cooling and other processes. Galvanized iron wire should pay attention to the following points in the use process:

Galvanized wire A stable layer of zinc is coated on the outside of the wire, which is used to protect the wire and make the wire service life longer. When producing galvanized wire, the wire is pickled. Pickling is to use some acid mist or acid to wash off some oxides on the surface of iron, that is, rust, and some other corrosive substances, to achieve the purpose of cleaning iron, so that zinc will fall off when galvanizing.

The use of electric welding mesh is very wide, can be used in many places. In the field of construction, especially the wall crack, has played a very important role, the traditional construction, is to put on mortar directly onto the wall, after such a long time, will appear fall off and fracture phenomenon, in order to prevent the occurrence of this phenomenon, must use welded wire mesh before rendering, welded wire mesh is fixed to the wall, above the plastering construction, Can ensure that the wall level for a long time, not easy to crack phenomenon.

The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.