1. Principle. Because zinc does not change easily in dry air, and in humid air, the surface can form a very dense film of zinc carbonate, which can effectively protect the interior from corrosion. And when the coating is damaged for some reason and the matrix is not too large, the zinc and steel matrix form a micro cell, so that the fastener matrix becomes the cathode and is protected. It is widely used in automobile transportation and other industries, but what is needed is the trivalent chromium passivation layer, zinc nickel alloy plating closed coating, reduce the harmful and toxic layer of hexavalent chromium passivation.

The strength of the hook mesh should be satisfied: when the vehicle is traveling at 80 kilometers per hour, the hook mesh will not fall into the river when it bumps against the rail at a 15 degree Angle. The shape and color of the hook mesh should be in harmony with the surrounding natural environment. The phenomenon planning of the important Bridges should be done well. When the bridge crosses important traffic lines, such as expressways, urban rail transit, expressways, railway trunk lines, etc., the hook mesh should add the protective mesh on the pavement of the bridge deck.

Welding mesh is widely used in industry, agriculture, breeding, construction, transportation, mining and other aspects. Such as machine shields, animal fences, flower fences, window fences, access fences, poultry cages, egg baskets and home office food baskets, paper baskets and decorative. We can make it according to the special requirements of customers. Welding mesh is made of high quality low carbon steel wire row welding, and then cold plating (electroplating), hot plating, PVC plastic coated surface passivation, plasticizing treatment, smooth mesh, uniform mesh, solid solder joint, local machining stable performance, corrosion resistance, corrosion resistance. Features: Stainless steel mesh selection of high quality stainless steel wire row welding, more acid, alkali resistance, solid welding, beautiful, widely used and so on.

When large rolls of galvanized wire are used to bind and reinforce the goods, corresponding binding methods should be selected according to the fastening node conditions of the strengthened goods, such as opening binding, opening binding, insertion binding and so on. The insulation layer of semi-hard and soft insulation products shall be based on the diameter of the steel pipe and the size of the equipment. Large rolls of galvanized wire or glue are tied together with a width of 60mm. The binding interval of semi-hard insulating products shall not exceed 300 mm; The larger length of felt and cushion shall not exceed 200mm, and the number of belts shall not be less than 2.

The impregnated hexagonal wire mesh will lose its original characteristics after corrosion, and will change in shape, color and mechanical properties, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment than dry environment easy corrosion, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated hexagonal wire mesh, prolong the service life of products.

The production process of large coil galvanized wire is relatively simple. The wire after cleaning is put into electroplating solution first. Of course, the plating solution should contain zinc oxide, a direct current of steel, another zinc plate in the plating solution. The zinc is transferred to the surface of the steel as a molecule. If it shows a bright and beautiful color, the wire is coated with zinc.

The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.