The corrosion or discoloration of galvanized iron wire in the atmosphere caused by oxygen, moisture and other pollution impurities is called rust or rust. After galvanized iron wire rusting, it will affect the appearance quality, seriously affect the use, and even cause scrap, so galvanized iron wire must be properly kept and pay attention to rust prevention.

At present, there are two processing methods of blade stabbing rope. One is to make it into a spiral shape, and then make a clip treatment. It is not only our common spiral blade stabbing rope, but also a single spiral blade stabbing rope without clip, but even a single helix can not stretch it to a relatively straight. This is mainly because the blade barbed rope is wrapped and wound at the same time, so it can only be spiral.

Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.

The blade gill net has 3-7 buckles every 2 turns, and it is a circle card. After being opened, it forms a spiral shape. When stretching, you must take protective gloves to prevent scratches. When opening, only one side of the gill net needs to be fixed, and then the gill net needs to be opened in the opposite direction. Pay attention to the spacing of the holes should not be too large, otherwise it will affect the aesthetic effect. As long as the time to slowly return to the line, simple operation, convenient construction.

Annealing wire is widely used because it has a good elasticity and flexibility, in the annealing process can be good control of its hardness, it is mainly made of iron wire, more often used in the construction industry binding wire use. In the production of the wire factory, annealing wire will be processed according to the properties of the material, according to the needs of different to change its hardness degree, can make it has more advantages, can reduce the consumption of metal, reduce the cost of production.

Now it is more used in the binding of the construction industry. Compared with ordinary wire, it is also softer and has better luster. Use in daily life does not need to carry out maintenance and maintenance, saving a lot of time, but also save the cost of maintenance and maintenance. Annealed wire has good stability, good corrosion resistance, greatly prolonging the service life. There are many kinds, which can be selected according to different uses. The device for making annealed wire is simple, and the utilization rate of the device is improved. The material properties of annealed wire can meet different processing needs.

The methods to control the thickness of galvanizing are as follows: you can slow down the lifting speed of the workpiece, control the time of galvanizing as far as possible, add the appropriate amount of thinning alloy, reduce the thickness, and improve the temperature of hot-dip galvanizing. But consider the zinc pot, iron pot should not exceed 480 degrees, ceramic pot can be 530 degrees, which can reduce the time of zinc immersion.

The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

It is very important to know the important guarantee of railway transportation, because most of the enterprises now choose the mode of transportation is railway transportation, and railway as an important means of transportation for people to go out, its safety is a social concern. At this time the blade thorn rope can play a very good practical value in various railway trunk lines.