This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.

Summer is the breeding season of mosquitoes, at this time, not only should pay attention to pet food and drinking water clean, but also pay attention to cleaning the dog cage regularly, so as to avoid pet disease.

Large roll galvanized wire is simply galvanized iron wire, usually used wire is often visible, because iron is very easy to be corroded and rusted, so it is necessary to put a layer of other not easy to rust metal plating in the outer layer, to achieve the effect of corrosion resistance and rust resistance, the effect of zinc can do more. Therefore, many customers often require hardware factories to produce galvanized iron wire, which requires the use of galvanized iron wire equipment.

The advantage of galvanized iron wire after annealing: after annealing increases the elongation of the iron wire. Makes the product softer and increases the range of application. After electric galvanizing hot dip galvanizing. Copper electroplating is widely used and screen production. Galvanized iron wire is a soft iron wire product processed by low carbon steel wire through cold drawing, heating, constant temperature, and even heat preservation. Generally, the quality of ordinary galvanized iron wire will be relatively soft, the softness is relatively balanced, and the color is consistent. It is mainly used in construction, mining, chemical industry and so on.

Because of the corrosion resistance of zinc layer, can be applied to all kinds of environment, it is also very convenient to use, has been a more popular hardware products. Galvanized iron wire should pay special attention to the acyl wash, to slowly into the container, to prevent acid sputtering on the body, at the same time prohibit the water into, so it is easy to let the acid out, to learn to handle lightly, stacking should also be firm and neat. It can be widely used in construction, handicrafts and other daily civilian applications.

There are three methods to detect the thickness of zinc layer of galvanized wire: weighing method, cross section microscopy method and magnetic method, among which the first two experiments will cause certain damage to galvanized wire, including the length of galvanized wire and the reduction of dosage. The general detection of galvanized wire galvanized layer is detected by magnetic method, which is also a more intuitive and convenient method. The standard of galvanized layer thickness is related to the wire diameter of galvanized wire. The larger the wire diameter of galvanized wire, the thicker the galvanized layer is. It is the thickness of galvanized layer and cast iron after centrifugal separation.

Spray powder mainly acrylic powder, polyester powder and so on. Dipping is a kind of plastic coating process, that is, the plastic coating on the matrix, generally metal, such as: daily use of clothes hangers, pliers handles, scissors on the rubber sleeve, various handrails, etc. Plastic immersion is to heat the metal to spray plastic powder evenly on the metal to form a plastic film, or heat immersion liquid into the metal to cool it and then plastic coating on the metal surface.

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, The softness is also very uniform, the color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry, etc.

Galvanized wire is processed from low carbon steel wire rod, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes. Galvanized wire is widely used. Electroplating temperature should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

Since galvanized iron wire will rust, we need to pay attention in the process of storage and use, try to store in a dry and ventilated environment, in the process of use to avoid damaging the surface of galvanized iron wire, we can slow down the time of galvanized iron wire rust.