For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by customers. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this thing is more important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized silk, the weight can reach 300kg/ roll or 800kg/ roll.

Stainless steel blade barbed rope under normal circumstances, basically 20 or 30 years is no problem, but because of the problem of its own material will appear a certain degree of rust, this is also because usually stainless steel blade barbed rope used by the material is 304 material, in daily use if in a long-term humid environment will cause certain corrosion. But usually users buy stainless steel blade barbed rope is basically life will not have problems users can also rest assured to use.

Many people do not know how to choose high quality cut wire, I will give us a detailed introduction. The raw material of cutting wire is divided into: stainless steel cutting wire, copper cutting wire, steel wire cutting wire, copper plated steel wire cutting wire, galvanized steel wire cutting wire, iron wire cutting wire, aluminum wire cutting wire and so on.

Galvanized iron wire will rust, mainly and the thickness of galvanized layer and the use of the environment, galvanized iron wire is also divided into cold galvanized iron wire and hot galvanized iron wire, in general, hot galvanized iron wire galvanized layer is thicker, rust prevention time is longer, generally can be 7 or 8 years without rust. If the galvanized layer is damaged, or long-term use in a humid environment, it will accelerate the rust time of galvanized iron wire.

For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by the customer. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this is very important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized wire, the weight can reach 300kg/ roll or 800kg/ roll.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

5, according to the wire diameter thickness to adjust zinc dipping time

1. Principle. Because zinc does not change easily in dry air, and in humid air, the surface can form a very dense film of zinc carbonate, which can effectively protect the interior from corrosion. And when the coating is damaged for some reason and the matrix is not too large, the zinc and steel matrix form a micro cell, so that the fastener matrix becomes the cathode and is protected. It is widely used in automobile transportation and other industries, but what is needed is the trivalent chromium passivation layer, zinc nickel alloy plating closed coating, reduce the harmful and toxic layer of hexavalent chromium passivation.

With the increasingly extensive use of hook mesh, the method of bridge rail is also different. The height of sidewalks or seatbelt outer railings should not be lower than 1.10 metres. The net distance between railings should not be greater than 140 mm and horizontal bar rails should not be used. The planning of the hook mesh is necessary to be safe and reliable, the bolt should be installed on the basis of the railing, its strength should meet the requirements of the standard.

The advantages of the blade stabbing rope (1) lightweight, high strength, never rust, good softness, fatigue resistance, impact resistance, breaking force, the overall structure is strong and durable, the service life is more than 30 years; (2) Close to nature, green environmental protection, highly effective protection of bird feathers and animal skin, effectively prevent rodents and other animals from biting, to give animals a safe and comfortable living environment; (3) Good visibility through l, luxurious appearance, novel style, itself is a big landscape. We can send you samples and make sure they are consistent. Our TECHNICIANS and ENGINEERS can also visit our factory free of charge for site investigation and design. According to your requirements and specific application environment, we can provide detailed material, rope diameter, hole distance and overall structure advice to guide installation.

Cold drawing wire is a metal cold processing, with wire rod as raw material, that is, the mouth of the steel bar. Cold drawing wire is a product produced by a series of processes such as shell stripping, which is a common wire. In the development and production of metal materials, cold drawing wire is a very common material, its performance is good, the range of use is very wide, manufacturers in processing are the use of cold processing to produce.

Purpose of galvanized hexagonal net: building wall fixed, heat preservation, heat insulation; Power plant tied pipe, boiler warm; Anti-freezing, residential protection, landscaping protection; Raising chickens and ducks, isolating chicken and duck houses, to protect poultry; To protect and support seawalls, hillsides, roads and Bridges and other waterworks.

Wet air in rain and snow climate, steel mesh sheet exposed, easy to rust, to avoid affecting the use of steel mesh, it is necessary to carry out simple rust prevention treatment, of course, slight rust float will not affect the use of steel mesh. Common network site storage, rainy days, heavy snow, rainy days and rainy days, how to better save the steel mesh, this is a lot of friends need to consider.