The application of black iron wire in the process is mainly through the hot metal billet rolled into 6.5 mm wire rod, and then put it into the wire drawing device into a different diameter line, and then gradually reduce the aperture of the wire drawing disk, cooling and annealing, coating and other processes, made into a variety of different specifications of iron wire, this kind of iron wire and ordinary black iron wire compared, will be softer, Softness is also very uniform, color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.

Zinc dipping time should be adjusted according to the thickness of wire diameter. The method of adjustment is to use the lead screw above the zinc pot, the length of the distance to the ceramic sinking roller. Thick wire diameter zinc dipping time should be long, fine wire diameter zinc dipping time should be short, zinc dipping length is in the range of 2~3.5m, which is also to reduce the zinc consumption of steel wire, is an aspect of maintaining the uniformity of zinc layer.

Stainless steel blade barbed rope under normal circumstances, basically 20 or 30 years is no problem, but because of the problem of its own material will appear a certain degree of rust, this is also because usually stainless steel blade barbed rope used by the material is 304 material, in daily use if in a long-term humid environment will cause certain corrosion. But usually users buy stainless steel blade barbed rope is basically life will not have problems users can also rest assured to use.

Cold galvanizing (galvanizing) is in the plating tank after the current unidirectional, so that the zinc gradually plated on the metal surface, slow production speed, uniform coating, thin thickness, usually as long as 3-15g, bright appearance, poor corrosion resistance, usually a few months will rust. Compared with hot dip galvanizing, the production cost of electric galvanizing is lower.

3, reduce the bivalent iron ion in the plating aid used for hot plating wire, reduce the formation of zinc slag

Cold wire drawing is a kind of cold processing of metal. The raw material is wire rod, which is produced by peeling, galvanizing and other processes. Galvanized cold drawing is used more in building materials. Its testing standards are also different. The strength of cold drawing is relatively high. Because of the high strength of steel, it plays a very important role in construction. It saves the construction steel in building materials, and also reduces the cost of the project. It also plays a very important role in the structure of concrete.