Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.

Stainless steel hexagonal network is composed of machine will be produced stainless steel wire of a kind of metal mesh, not easy corrosion, the survival of the fixed number of year is longer, net of wide, coarser size, strong practicability, flexibility and other unique places, stainless steel hexagonal wire netting material is stainless steel wire, wire diameter because stainless steel wire big viscosity of large stainless steel hexagonal network would be hard to manufacture, Of course, it is more difficult to hold the edge or twist the edge, so stainless steel hexagonal mesh whether from the material or artificial are expensive, but stainless steel hexagonal mesh will not rust and use years is also very long, appearance without disposal can achieve the use effect.

The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.

The development of iron wire industry in our country is still very good, among which there is a kind of iron wire called large roll galvanized wire, which is also widely used with its own good performance. In fact, the zinc layer plays a protective effect on the iron wire inside, which can ensure that the iron wire is not oxidized, and it is convenient and beautiful to use. Galvanized iron wire is formed by pickling, high temperature, hot dip galvanizing and other steps. It has good toughness and elasticity and can be applied to many civil fields.

With the improvement of people’s living standard, pet raising is becoming more and more common. Pets also need a comfortable environment, so pet cage is an ideal choice for pet raising. Dogs are loyal friends of human beings. They will accompany you all your life and protect you until you die. Raising small animals can bring comfort to lonely old people; Patients who receive visits from animals can improve their depressed moods and even relieve pain. Families with pets add joy and cohesion; Companion animals usually form familial bonds with their owners.

There are still some differences between electric mesh and wire mesh and steel mesh. This mesh is mainly a welding mesh made of high quality low carbon steel wire after straightening and cutting, and then welded by electric welding equipment. It can be said that because of the characteristics of fast production and convenient transportation, it has been applied in many industries. In today’s construction projects, people can also see the image of this network well. The application of welded mesh in this industry is mentioned because of its strong corrosion resistance and uniform mesh. It has become a special grid for floor heating in construction industry and has been applied in many fields.

When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.

3. Acid activation acid activation solution should be able to remove corrosion products and oxide film (skin) on the surface of parts, without excessive corrosion on the matrix.

Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.