Post time: 07-05-22- 2, pasture installation of thorn rope spacing, if it is cattle or horses due to the larger size, the spacing can be appropriately relaxed. But if it’s a sheep, it’s a smaller animal and you have to make it a little bit narrower.
- 3. The front and back twist barbed wire has a beautiful appearance
2, reduce the bivalent iron ion in the plating aid used for hot plating wire, reduce the formation of zinc slag
The galvanized layer forms a special metallurgical structure that can withstand mechanical damage during transportation and use. Selection of low carbon raw materials, through wire drawing, annealing processing, soft and strong tensile resistance. Finished products coated with anti-rust oil, not easy to rust, according to customer requirements into bundles, each bundle of 1-50Kg, can also be made into U-shaped wire, broken wire, internal plastic and external hemp packaging, mainly used for binding silk, construction silk, etc.
The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.
Post time: 04-11-22People who want to keep birds for the long term need to know how to choose the right cage and how to raise them scientifically. It’s all about the birds’ daily life and health. Only by knowing more about the various aspects of raising birds can they be raised healthy and lively, singing freely and suitable for viewing.
1. Grid structure is simple, beautiful and practical; 2. Easy to transport, installation is not limited by terrain relief; 3. Especially for mountain, slope, multi-curved area adaptability; 4. Medium low price, suitable for large area use. Main market: railway, highway closed net, yard fence, residential guardrail, all kinds of isolation net.
Cold drawing wire is a metal cold processing, with wire rod as raw material, that is, the mouth of the steel bar. Cold drawing wire is a product produced by a series of processes such as shell stripping, which is a common wire. In the development and production of metal materials, cold drawing wire is a very common material, its performance is good, the range of use is very wide, manufacturers in processing are the use of cold processing to produce.
Post time: 05-07-221, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.
- The effect of chemical composition and metallographic structure of steel wire
There is also a straight blade stabbing rope, which is mainly because the board and wire are not wound in the process of wrapping, so the blade stabbing rope produced is a straight product. The length of the barbed rope of this specification cannot be too long due to the limitation of logistics, and it cannot be bent because it is easy to be deformed by force. This is also the main reason why the barbed rope of the straight blade is not whole or long. Customers are advised to determine the spacing before purchase to prevent losses caused by no calculation.
Because of the high carbon content, simple cracks occur during water quenching, so double liquid quenching (water quenching + oil cooling) is mostly used, and oil quenching is mostly used for small cross section parts. This type of steel is generally used after quenching by medium temperature tempering or normalizing or in the surface quenching state. Mainly used for manufacturing spring and wear-resistant parts.
The different spacing of the thorn rope is mainly in order to save costs to consider, because if they are too close, then obviously a little waste of resources, but the installation is too sparse will not work. Usually the bottom spacing is about 10cm, and the top is up to 20cm, this is because the higher the place is more difficult to climb over, usually more than one meter without the help of tools it is difficult for ordinary people to climb over, and the bottom because of the relatively tight can prevent personnel from drilling in the past.
Post time: 15-11-22- Ring corn with: used as a ring corn net, generally use mesh 5cm*7cm or 5cm*5cm of the original galvanized welding net, wire diameter from 1.8mm-2.3mm, height of 1.2m – 1.8m.
With a large pickpocket used for steel wire, into the zinc liquid before the surface of the zinc ash stirring; Use a small outlet for galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. The extracted zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the biggest steps to bring zinc consumption down, and it’s a real problem, one that hasn’t been solved for years.
According to the different requirements of the industry, different weights of alloy ingots are put in the smelting furnace according to the standard, such as weaving, Ming, paper, lang, silicon, etc., and the data out of this smelting is called gold ore iron. Iron has gray iron, white iron and the above-mentioned gold, they have different characteristics, so in the industry according to their different characteristics to transport and selection. For example, in gray iron, its carbon exists in iron ore in graphite condition, the crack is often gray, soft and strong, simple filtering, suitable for casting.
According to the different technology is divided into different types, you can choose according to your own needs. Has good flexibility and elasticity, the main role of annealing wire is to control its degree of softness and hardness, when the annealing wire is made of steel wire, now more used in the construction industry bundle use, compared with ordinary iron wire is also softer, has a better luster.
- Barbed rope often appears in another model: 14*14# barbed rope, 12*12# barbed rope, 12*14# barbed rope, among which the diameter of 14# wire is about 2.0 mm, the diameter of 12# wire is about 2.65 mm, there is a non-standard 2.25 mm is also commonly used line. According to this specification, a kilogram of 14*14# barbed rope is 12 meters, a kilogram of 12*14# barbed rope is 8 meters, and a kilogram of 12*12# barbed rope is about 5 meters.
Welding mesh is also known as external wall insulation wire mesh, galvanized wire mesh, galvanized welding mesh, wire mesh, row welding mesh, touch welding mesh, construction mesh, external wall insulation mesh, decorative mesh, barbed wire, square eye mesh, screen mesh, anti-crack mesh. Stainless steel welding net, is made of high quality stainless steel wire row welding, more acid resistance, alkali resistance, solid welding, beautiful, wide use and so on.
Post time: 10-05-23Galvanized wire is processed by low carbon steel wire rod. It is made of low carbon steel, after drawing forming, pickling and rust removal, high temperature annealing, hot dip galvanizing, cooling and other processes. Electrogalvanized iron wire using low carbon steel as raw materials, after drawing, galvanized and other processes completed. It has the characteristics of galvanized layer, strong corrosion resistance, strong galvanized layer, and so on. Galvanized iron wire is widely used in construction, highway walls, Zahua, weaving and other industries.
Temporary rust prevention is to prepare for the completion of the mission of the protective layer to be removed. The methods include: cajoling corrosion inhibitors, coating antirust oil, peeling molecular compound plastics, drying air, vacuuming, etc. Change the internal structure of the metal: new chromium, nickel and other alloy elements made of stainless steel, but the alloy is not much, expensive, difficult to produce widespread application.