Some large roll galvanized wire products in order to meet different industrial needs, will be further processed on the surface, such as the anti-corrosion layer, galvanized, iron plating, aluminum alloy plating, or in the galvanized wire appearance above the copper plating, brass plating, etc., to strengthen the steel wire and colloidal years and capabilities. Generally, galvanized wire products should be well plated and drawn when they are produced, and the sequence of the two processes should be decided according to the production or industrial needs.

The application of black iron wire in the process is mainly through the hot metal billet rolled into 6.5 mm wire rod, and then put it into the wire drawing device into a different diameter line, and then gradually reduce the aperture of the wire drawing disk, cooling and annealing, coating and other processes, made into a variety of different specifications of iron wire, this kind of iron wire and ordinary black iron wire compared, will be softer, Softness is also very uniform, color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry.

Although galvanized iron wire has the protection of galvanized layer, it does not say that it will not rust at all, but delays the time of rust. In general, cold galvanized iron wire can be kept for 1-2 years without rust, hot galvanized iron wire can be used for 8-10 years without rust. If properly maintained, the use time will be longer. So how to prevent galvanized iron wire rust?

The hot plating wire is made of low carbon steel wire rod, which is processed by drawing forming, pickling and rust removal, high temperature annealing, hot dip galvanizing and cooling. Galvanized iron wire has resistance and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Widely used in construction, handicrafts, wire mesh, highway guardrail, commodity packaging and ordinary civilian and other fields.

Hot dip galvanizing is in the hot melt zinc liquid dip plating, production speed, thick but uneven coating, the market allows the low thickness of 45 microns, up to 300 microns above. It is dark in color, consumes more zinc metal, forms infiltration layer with base metal, and has good corrosion resistance. Hot dip galvanizing can be maintained for decades in outdoor environment.

Annealed wire is mainly made of soft iron wire through low carbon steel heating, hot drawing, constant temperature and other processes. Because of the differences in use, there are also different in the production process, and the specifications are varied. Annealed wire can be widely used, mainly because annealed wire and other kinds of wire, has many advantages.

Customers do not need to worry about the impact of the production cycle when ordering products from the thorn rope factory, because the overall treatment is now focused on the waste gas, so the production of thorn rope should be said to have the least impact. Customers ordering products in the thorn rope factory can rest assured that the delivery time this piece, can provide customers with goods on time. If the production cycle is not affected, then customers will be more assured of the thorn rope factory.