In the calculation process of 12*14 specifications of barbed rope, it can not be calculated according to the above calculation formula, because first of all, two specifications of raw materials are used, the thinner the wire diameter, the higher the processing cost. Generally speaking, a kilogram of 12*14 barbed rope can reach about 7.5 meters, and the ratio of warp wire to barbed rope cannot be calculated according to the traditional ratio of 7 to 3. The specific use of how much wire and silk need to go through a series of professional measurement but also increase the loss of raw materials and other factors to calculate. Thorn rope factory will also according to customer needs to calculate the reasonable amount of customer use.

In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.

The insulation layer of large rolls of galvanized wire and rigid thermal insulation products can be bound with double strands of galvanized iron wire, and the binding interval shall not exceed 400mm. The pipe or corresponding equipment with nominal diameter equal to or greater than 600mm shall stop reinforcement after binding, and the enclosed galvanized steel wire must be winched. The iron or wood rod should be tightened, but the tightening level should be moderate, not too tight or too loose, and not damage the wire. The consumption of wire and steel wire is generally used in drawing process and galvanized disposal.

Poor pretreatment before electroplating; Bath temperature is too low; Poor quality additives or excessive additives and organic impurities can cause poor bonding. The quality of the additive also has an effect on coating foaming. Some additives react incompletely during synthesis and continue to polymerize during long-term storage or use. The additive tends to distort the lattice and create stress, causing the coating to blister.

The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.

In general, the cost of hot dipping zinc is lower than that of other maintenance coatings. The reason is very simple. Other maintenance coatings, such as sand painting, are labor-intensive processes, whereas hot dipping zinc processes are highly mechanized and tightly controlled in-plant construction. Hot dip zinc coating can be visually and briefly tested for non-destructive coating thickness.

What kind of wire mesh fence should be used for chickens, ducks, geese and other light poultry? The so-called good refers to the high cost performance, that is, the use effect can be achieved, such as the size of the mesh, the size, etc., and the cost can be reduced to the greatest extent.

With the improvement of living standards and the reduction of family size, keeping pets is becoming a way of life for many people. According to statistics, the number of pet dogs has reached more than 100 million, and the trend is increasing rapidly every year. Beijing alone had more than 900,000 licensed dogs in 2010, according to a survey, and the number of pet cats is also very large.

The application of electric welding mesh is more widely, at present, it has replaced the use of other parts of the screen, the cost of electric welding mesh is low, the production speed is very fast, so it is very popular. The treatment required before galvanized welding mesh is recrystallization annealing, because the welding mesh must maintain an oxide and no other impurities of pure iron active surface, if you can’t keep its surface clean will lead to poor galvanized effect, galvanized layer and iron material is not tightly combined, so this step is necessary.

Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

No matter how good the quality of hot-dip galvanized barbed rope is, it is only attached to the surface of the wire with galvanized layer, and with the cause of chemical reaction, the zinc layer on the surface will gradually lose its effect because of oxidation reaction, which is more prominent in the humid area of the environment. And because, after all, the wire will rust, so the quality of hot-dip galvanized barbed rope is certainly not up to the level of stainless steel barbed rope.

Steel wire and iron wire have many similarities, but carefully distinguish, will find that they are not only different in the material, but also in the product characteristics of the great difference. So when choosing, be sure to make a clear distinction between the two. Steel wire factory introduces steel wire carbon structural steel made above, generally not galvanized, used for machinery, spring. Black, very hard; Wire: made of mild steel (mild steel), galvanized, used for joining and binding. White and soft.

The main raw material of blade barbed rope is galvanized wire and galvanized sheet, because the price of galvanized sheet is more expensive than galvanized wire, so it is directly reflected in the price of the sales of blade barbed rope. There is also the difference in processing technology also led to the difference in the price of the blade thorn rope. The traditional barbed rope is mechanically twisted, which uses less labor and has high production efficiency. But the blade is after two mechanical processing in the manual processing operation before the appearance. So whether from the labor force or from the production efficiency also said there is a large gap. These factors lead to the price of blade thorn rope is more expensive the main factor.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.