Specific requirements for the safety of galvanized wire production: clean up all tools and other objects that hinder production in the galvanized wire production environment. Operators in the pickling process, pay attention to the action should be careful, not careless, into the pickling tank must be handled lightly, to prevent splashing on the body. When adding acid, the acid must be slowly poured into the water. It is forbidden to pour the water into the acid, so as to prevent the acid from splashing out and hurting people. Do not hurt yourself or others.

Raw material of wire mesh sheet cold drawn low carbon steel wire base material can choose low carbon steel hot rolled disk bar or hot rolled smooth steel bar. The base material number and diameter of cold-drawn low carbon steel wire can be confirmed according to the rules in the table below. During the cold drawing process, the surface shrinkage rate of each drawing should not be greater than the wire mesh before cold drawing. Annealing shall not be carried out during wire drawing. If butt welding is required, the same production unit and base material of the same number should be selected. The appearance quality of wire mesh should not affect wire drawing. When the welding function is poor or brittle fracture occurs, special inspection should be carried out according to relevant standards.

Because of the large size of the  barbed rope, the rope factory is used to packing. If you do not pack, then a load of blade rope can not hold many pieces, but also relatively occupy space and easy to be lost in the process of transportation.

Spring wire shall have high tensile strength, elastic limit, endurance and fatigue strength, and be resistant to shock and oscillation. The objectives of strength and endurance, especially the prevention of alteration cracks, are key to the consumption of spring steel wires. The inner and outer quality of wire rod directly affect the function of steel wire.

Cold galvanizing is also called electric galvanizing. It is the use of electrolytic equipment to remove oil, pickling, and then put the pipe into the solution of zinc salt, and connect the anode of the electrolytic equipment, place zinc plate on the opposite side of the pipe, and connect the positive pole of the electrolytic equipment to the power supply. A layer of zinc is deposited on the pipe fitting by directional movement of an electric current from the positive pole to the negative pole. Cold plated pipe fitting is processed before galvanizing.

Different from the general zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach the former 6-8 times, so in the service life also has a great advantage, ordinary products three or five years began to corrosion and the latter will take longer to change. Stainless steel barbed rope is in the material aspect of protection, so the durability is also better, these two products are long in the service life, but in the price is high.

In strict accordance with the multi-pass small compression rate drawing, the total compression rate is 96.48%, reducing the scraping of zinc layer. The whole wire drawing die is made of tungsten steel die and polycrystalline die. The Angle of the working cone of the wire drawing die is 12° ~ 16°, and the length of the sizing belt is 0.15 of the diameter of the wire, so as to ensure that the deformation of the zinc layer is basically synchronous with the steel wire substrate.