Although galvanized iron wire has the protection of galvanized layer, it does not say that it will not rust at all, but delays the time of rust. In general, cold galvanized iron wire can be kept for 1-2 years without rust, hot galvanized iron wire can be used for 8-10 years without rust. If properly maintained, the use time will be longer. So how to prevent galvanized iron wire rust?

The welding process of galvanized steel wire mesh because of low carbon steel carbon content is low, manganese and silicon content is low, will not occur severe hardening or quenching structure due to welding. The low carbon steel joints have excellent plasticity and impact toughness after welding. In the welding process, it is generally not necessary to preheat, interlayer temperature control, post-heating control and heat treatment to improve the welding structure.

(1) The application method of packaging and binding galvanized shaft wire ordering: ① the pulling position on the goods should be reasonably selected. When used to avoid horizontal movement of goods, the pulling position should be as low as possible; When used to avoid overturning the goods, the pulling position can be appropriately high. ② The use of galvanized iron wire [1] pull reinforcement methods mainly include: figure eight, inverted figure eight, cross, zigzag or reverse zigzag and so on. Various pull methods can be used alone, but also two or more than two kinds of use. The pull should be as symmetrical as possible. (3) When pulling reinforcement, the single or double strands of galvanized iron wire will reciprocate around the goods and vehicles between the two tying nodes, and should be pulled tight galvanized iron wire so that the tightness of each strand is as common as possible, and some of the remaining cross around its own rope rod, and the rest of the tail toward the car.

6, according to the wire diameter thickness to adjust zinc dipping time. Zinc dipping time should be adjusted according to the thickness of wire diameter. The method of adjustment is the length of the distance between the lead screw on the zinc pot and the ceramic sinking roll. The zinc dipping time of coarse wire diameter should be long, and the zinc dipping time of fine wire diameter should be short.

Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When the galvanized wire out of light plating should be carried out light treatment, the galvanized wire bath to control the temperature. Now the quality level of galvanized wire on the market is not equal, galvanized wire is also called hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities.